Home > News
Introduction
Sintered iron bearings(iron powder), made of iron powder as base material, are produced by the process of being pressed in mold, sintered in high temperature and absorbed oil in vacuum. They are widely used in the applications of automotive, motor cycle, office equipment and electronic tool due to the advantages of good self-lubricating,good wear resistance and stable size.
Chemical Composition%
|
Material coda/ MPIF standard |
Fe |
Cu |
Sn |
C |
graphite |
other |
|
F-0000-K15 |
96.2-100 |
0-1.5 |
/ |
0-0.3 |
/ |
0-2.0 |
|
F-0000-K23 |
96.2-100 |
0-1.5 |
/ |
0-0.3 |
/ |
0-2.0 |
|
F-0005-K20 |
95.9-99.7 |
0-1.5 |
/ |
0.3-0.6 |
/ |
0-2.0 |
|
F-0005-K28 |
95.9-99.7 |
0-1.5 |
/ |
0.3-0.6 |
/ |
0-2.0 |
|
F-0008-K20 |
95.6-99.4 |
0-1.5 |
/ |
0.6-0.9 |
/ |
0-2.0 |
|
F-0008-K32 |
95.6-99.4 |
0-1.5 |
/ |
0.6-0.9 |
/ |
0-2.0 |
|
FC-0200-K20 |
93.8-98.5 |
1.5-3.9 |
/ |
0-0.3 |
/ |
0-2.0 |
|
FC-0200-K34 |
93.8-98.5 |
1.5-3.9 |
/ |
0-0.3 |
/ |
0-2.0 |
|
FC-1000-K20 |
86.7-91.0 |
9.0-11.0 |
/ |
0-0.3 |
/ |
0-2.0 |
|
FC-1000-K30 |
86.7-91.0 |
9.0-11.0 |
/ |
0-0.3 |
/ |
0-2.0 |
|
FC-1000-K40 |
86.7-91.0 |
9.0-11.0 |
/ |
0-0.3 |
/ |
0-2.0 |
|
FC-2000-K25 |
75.7-82.0 |
18.0-22.0 |
/ |
0-0.3 |
/ |
0-2.0 |
|
FC-2000-K30 |
75.7-82.0 |
18.0-22.0 |
/ |
0-0.3 |
/ |
0-2.0 |
|
FC-2000-K40 |
75.7-82.0 |
18.0-22.0 |
/ |
0-0.3 |
/ |
0-2.0 |
|
FC-0205-K20 |
93.5-98.2 |
1.5-3.9 |
/ |
0.3-0.6 |
/ |
0-2.0 |
|
FC-0205-K35 |
93.5-98.2 |
1.5-3.9 |
/ |
0.3-0.6 |
/ |
0-2.0 |
|
FC-02058-K25 |
93.2-97.9 |
1.5-3.9 |
/ |
0.6-0.9 |
/ |
0-2.0 |
|
FC-02058-K40 |
93.2-97.9 |
1.5-3.9 |
/ |
0.6-0.9 |
/ |
0-2.0 |
|
FC-0508-K35 |
91.1-95.4 |
4.0-6.0 |
/ |
0.6-0.9 |
/ |
0-2.0 |
|
FC-0508-K46 |
91.1-95.4 |
4.0-6.0 |
/ |
0.6-0.9 |
/ |
0-2.0 |
|
FC-2008-K44 |
75.1-81.4 |
18.0-22.0 |
/ |
0.6-0.9 |
/ |
0-2.0 |
|
FC-2008-K46 |
75.1-81.4 |
18.0-22.0 |
/ |
0.6-0.9 |
/ |
0-2.0 |
|
FCTG-3604-K16 |
54.2-62.0 |
34.0-38.0 |
3.5-4.5 |
0.5-1.3 |
/ |
0-2.0 |
|
FCTG-3604-K22 |
54.2-62.0 |
34.0-38.0 |
3.5-4.5 |
0.5-1.3 |
/ |
0-2.0 |
|
CFTG-3806-K14 |
50.2-58.0 |
36.0-40.0 |
5.5-6.5 |
0.5-1.3 |
/ |
0-2.0 |
|
CTFG-3806-K22 |
50.2-58.0 |
36.0-40.0 |
5.5-6.5 |
0.5-1.3 |
/ |
0-2.0 |
|
FG-0303-K10 |
94.5-98.0 |
/ |
/ |
0-0.5 |
2.0-3.0 |
0-2.0 |
|
FG-0303-K12 |
94.5-98.0 |
/ |
/ |
0-0.5 |
2.0-3.0 |
0-2.0 |
|
FG-0308-K16 |
94.5-98.0 |
/ |
/ |
0.5-1.0 |
1.5-2.5 |
0-2.0 |
|
FG-0308-K22 |
94.5-98.0 |
/ |
/ |
0.5-1.0 |
1.5-2.5 |
0-2.0 |
Physical Properties
|
Material coda/ MPIF standard |
Strength Coefficient |
|||
|
103psi |
Mpa |
Oil content % |
Density (g/cm3) |
|
|
F-0000-K15 |
15 |
100 |
21 |
5.6-6.0 |
|
F-0000-K23 |
23 |
160 |
17 |
6.0-6.4 |
|
F-0005-K20 |
20 |
140 |
21 |
5.6-6.0 |
|
F-0005-K28 |
28 |
190 |
17 |
6.0-6.4 |
|
F-0008-K20 |
20 |
140 |
21 |
5.6-6.0 |
|
F-0008-K32 |
32 |
220 |
17 |
6.0-6.4 |
|
FC-0200-K20 |
20 |
140 |
22 |
5.6-6.0 |
|
FC-0200-K34 |
34 |
230 |
17 |
6.0-6.4 |
|
FC-1000-K20 |
20 |
140 |
22 |
5.6-6.0 |
|
FC-1000-K30 |
30 |
210 |
19 |
5.8-6.2 |
|
FC-1000-K40 |
40 |
280 |
17 |
6.0-6.4 |
|
FC-2000-K25 |
25 |
170 |
22 |
5.6-6.0 |
|
FC-2000-K30 |
30 |
210 |
19 |
5.8-6.2 |
|
FC-2000-K40 |
40 |
280 |
17 |
6.0-6.4 |
|
FC-0205-K20 |
20 |
140 |
22 |
5.6-6.0 |
|
FC-0205-K35 |
35 |
240 |
17 |
6.0-6.0 |
|
FC-02058-K25 |
25 |
170 |
22 |
5.6-6.0 |
|
FC-02058-K40 |
40 |
280 |
17 |
6.0-6.4 |
|
FC-0508-K35 |
35 |
240 |
22 |
5.6-6.0 |
|
FC-0508-K46 |
46 |
320 |
17 |
6.0-6.4 |
|
FC-2008-K44 |
44 |
300 |
22 |
5.6-6.0 |
|
FC-2008-K46 |
46 |
320 |
17 |
6.0-6.4 |
|
FCTG-3604-K16 |
16 |
110 |
22 |
5.6-6.0 |
|
FCTG-3604-K22 |
22 |
150 |
17 |
6.0-6.4 |
|
CFTG-3806-K14 |
14 |
100 |
22 |
5.6-6.0 |
|
CTFG-3806-K22 |
22 |
150 |
17 |
6.0-6.4 |
|
FG-0303-K10 |
10 |
70 |
18 |
5.6-6.0 |
|
FG-0303-K12 |
12 |
80 |
12 |
6.0-6.4 |
|
FG-0308-K16 |
16 |
110 |
18 |
5.6-6.0 |
|
FG-0308-K22 |
22 |
150 |
12 |
6.0-6.4 |