FLN2C-4005HT Iron Bronze Graphite Powder Metallurgy Bearing and Components

Standard: MPIF Standard 35
Code: FLN2C-4005HT
Type: Iron-Bronze Graphite Base
Products: Bearing & Parts
Product description: The FLN2C-4005HT heat-treated iron-bronze graphite powder metallurgy bearing adheres to MPIF Standard 35, with JIS-aligned specifications for automotive applications. This oil-impregnated, self-lubric
INQUIRY

FLN2C-4005HT Low-Alloy Steel (Ni-Mo-Mn-Cr, Heat Treated) Sintered Material

FLN2C-4005HT is the heat-treated version of FLN2C-4005 per MPIF Standard 35. Offers exceptional tensile strength and transverse rupture strength for the most demanding high-load PM applications.

Chemical Composition (MPIF Standard 35)

Element	Content
Fe	Balance
Ni	1.3–1.7%
C	0.4–0.7%
Mo	1.5–2%
Mn	0.4–0.6%
Cr	0.05–0.3%

Mechanical & Physical Properties

Property	Value
Density	6.7–7.4 g/cm³
Hardness	HRC 25–40
Tensile Strength (Ultimate)	790–1650 MPa
Tensile Strength (Yield)	450–1240 MPa
Impact Force	7–26 J
Transverse Rupture Strength	1280–2550 MPa

Material designation per MPIF Standard 35 — Material Standards for PM Structural Parts. Values shown represent the typical range across different density levels. HT suffix indicates heat-treated condition (quenching and tempering).